400mm e phahameng matla a graphite electrode
HP 400mm graphite electrode e haholo-holo entsoe ka petroleum coke le nale coke. Nako e lumelletsoeng ke 21000-31000A, 'me sekhahla sa hajoale se ka ba 16-24A/cm². Ka kakaretso e sebelisoa bakeng sa ho etsa tšepe ea matla a phahameng a sebōpi sa arc.
Motlakase oa matla a phahameng a graphite o entsoe ka coke ea boleng bo holimo ea petroleum, coke ea nale, sekontiri sa mashala le lisebelisoa tse ling tse tala tse etsang 66.88% ea litšenyehelo. Potoloho ea tlhahiso e feta matsatsi a 50, 'me matla a phahameng haholo a fihla ho matsatsi a 65. Ts'ebetso ea tlhahiso e kenyelletsa calcination, batching, kneading, ho bōpa, ho baka, ho pata, ho baka bobeli, graphitization le ho sebetsa.Hexi Carbon ke k'hamphani e hlahisang, e rekisang, e rekisetsang kantle le ho fana ka mefuta e mengata ea li-electrode tsa graphite tse matla haholo. Li-electrode tsa graphite tse matla tse hlahisoang ke k'hamphani ea rona li na le mehlala e nang le bophara ba 350mm ho isa ho 700mm eo u ka e khethang, le mefuta e meng ea li-electrode tsa graphite tseo u li hlokang le tsona li ka etsoa.
| Papiso ea Tekheniki Specification bakeng sa HPGraphite Electrode16″ | ||
| Electrode | ||
| Ntho | Yuniti | Mofani oa Mofani |
| Litšobotsi tse Tloaelehileng tsa Pole | ||
| Nominal Diameter | mm | 400 |
| Max Diameter | mm | 409 |
| Min Diameter | mm | 403 |
| Bolelele ba Lebitso | mm | 1800-2400 |
| Max Length | mm | 1900-2500 |
| Min Length | mm | 1700-2300 |
| Boima ba Bongata | g/cm3 | 1.68-1,73 |
| matla a tsheletseng | MPa | ≥11.0 |
| Young 'Modulus | GPA | ≤12.0 |
| Khanyetso e Itseng | µΩm | 5.2-6.5 |
| Tekanyo e phahameng ea hona joale | KA/cm2 | 16-24 |
| Bokhoni ba ho Jara ba Hona Joale | A | 21000-31000 |
| (CTE) | 10-6 ℃ | ≤2.0 |
| dikahare tsa molora | % | ≤0.2 |
| Litšobotsi tse Tloaelehileng tsa Nipple (4TPI/3TPI) | ||
| Boima ba Bongata | g/cm3 | 1.78-1,83 |
| matla a tsheletseng | MPa | ≥20.0 |
| Young 'Modulus | GPA | ≤15.0 |
| Khanyetso e Itseng | µΩm | 3.5-4.5 |
| (CTE) | 10-6 ℃ | ≤1.8 |
| dikahare tsa molora | % | ≤0.2 |